PENGARUH JUMLAH SPESIMEN DALAM UJI TEKAN MATERIAL GRAFIT IG-110 (Roziq Himawan1, Andryansyah2, Mudi Haryanto2, Darlis2)

Roziq Himawan, rh and Andryansyah, AD and Mudi Haryanto, MH and Darlis, DL (2019) PENGARUH JUMLAH SPESIMEN DALAM UJI TEKAN MATERIAL GRAFIT IG-110 (Roziq Himawan1, Andryansyah2, Mudi Haryanto2, Darlis2). In: Seminar Nasional Teknologi Energi Nuklir 2019 Padang, 18 September 2019 263 ISSN: 2355-7524, 18 September 2019, Universitas ANDALAS Fakultas Teknik Padang Sumatera Barat.

Full text not available from this repository.

Abstract

ABSTRAK
PENGARUH JUMLAH SPESIMEN DALAM UJI TEKAN MATERIAL
GRAFIT IG-110. High Temperature Gas Cooled Reactor (HTGR) merupakan salah satu
jenis Very High Temperature Reactor (VHTR) yang dikembangkan saat ini dan dikategorikan
dalam reaktor Generasi ke-4. Struktur utama teras reaktor HTGR mayoritas terbuat dari
material grafit. Tingginya temperatur dan tingginya paparan radiasi neutron berdampak pada
integritas material grafit. Salah satu pertimbangan dalam disain material grafit adalah sifat
mekanik kuat tekan. Oleh karena itu, penelitian ini bertujuan untuk memahami pengaruh
jumlah spesimen dalam uji tekan. Penelitian ini menggunakan spesimen yang terbuat dari
grafit isotropik nuclear grade IG-110. Spesimen uji tekan dibuat berbentuk kubus dengan
ukuran 10×10×10 mm. Uji tekan dilakukan menggunakan mesin uji tarik (Universal Tensile
Machine) Shimadzu dengan kapasitas 150 kN. Pengujian dilakukan dengan metode kendali
pergerakan cross head dengan nilai kecepatan 0,5 mm/min. Uji tekan dibagi menjadi tiga
kelompok, yaitu jumlah spesimen satu, dua dan tiga. Masing-masing kelompok pengujian
dilakukan sebanyak tiga kali. Hasil-hasil uji tekan menunjukkan bahwa setiap hasil pengujian
bervariasi dengan rentang nilai 78 MPa ~ 82 MPa. Namun, apabila masing-masing kondisi
pengujian, hasil pengujian dinyatakan dalam rerata, maka akan diperoleh hasil yang
mendekati konstan yaitu bernilai 80MPa. Dari hasil-hasil pengujian ini dapat disimpulkan
bahwa jumlah spesimen tidak memberikan pengaruh pada hasil uji tekan.
Kata kunci: High Temperature Gas Cooled Reactor, Grafit IG-110, Kuat Tekan
ABSTRACT
EFFECTS OF SPECIMEN NUMBER ON COMPRESSIVE STRENGTH OF IG-110
GRAPHITE MATERIAL. High Temperature Gas Cooled Reactor (HTGR) is one of Very High
Temperature Reactor (VHTR) types which have been developed and categorized into
Generation-4 reactor. The main structures of HTGR’s core are made of graphite materials.
High temperature and high flux of neutron exposure in HTGR reactor affects the integrity of
graphite materials. One of consideration in design using graphite material is it’s compressive
strength. It is therefore, the aim of this study is to acquire a knowledge of the effects of
specimen number in compressive test. The study was conducted using spesimen made of
isotropic nuclear grade graphite IG-110. The specimen size is 10×10×10 mm. Compressive
tests were conducted using Universal Tensile Machine Shimadzu with capacity of 100 kN.
Testings were conducted by controlling the cross-head displacement at constant velocity of
0.5 mm/min. Compressive tests are divided into three groups, each of which containing one,
two and three specimens in its respective group. The tests were conducted three times for
each specimen group. Compressive tests results show that the compressive strengths are
vary in the range of 78 MPa ~ 82 MPa. However, if it is presented in average, the results is
almost constant of 80 MPa. It is concluded that the number of specimen do not give a
significant difference and therefore the compressive strength is independent of the number
of specimens.
Keywords: High Temperature Gas Cooled Reactor, IG-110 Graphite, Compressive strength

Item Type: Conference or Workshop Item (Paper)
Subjects: Taksonomi BATAN > Keselamatan dan Keamanan Nuklir
Taksonomi BATAN > Keselamatan dan Keamanan Nuklir
Divisions: BATAN > Pusat Teknologi dan Keselamatan Reaktor Nuklir
IPTEK > BATAN > Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: Iskandar Alisyahbana Adnan
Date Deposited: 23 Jul 2020 00:25
Last Modified: 30 May 2022 08:40
URI: https://karya.brin.go.id/id/eprint/9896

Actions (login required)

View Item
View Item