ANALISIS METODE PEMBUATAN TERMOKOPEL TIPE-K PADA UNTAI FASSIP-02 (Arif Adtyas Budiman, G. Bambang Heru, Mulya Juarsa)

ABSTRAK
ANALISIS METODE PEMBUATAN TERMOKOPEL TIPE-K PADA UNTAI FASSIP-02.
Pengkajian sistem pendinginan pasif ini dilakukan melalui salah satu fasilitas uji di
laboratorium termohidrolik yang disebut sebagai Untai FASSIP-02. Terdapat 32 titik
pengukuran suhu, 1 titik pengukuran laju alir, dan tekanan operasi pada Untai FASSIP-02.
Setelah dilakukan pengujian pada setiap titik pengukuran suhu, terdapat beberapa
termokopel tipe-K yang mengalami penurunan kualitas pembacaan. Dalam kerangka
metode sirkulasi alami, besarnya perubahan suhu sebesar 1°C adalah siginifikan, sehingga
permasalahan pembacaan termokopel perlu ditindaklanjuti. Tindak lanjut ini dilakukan
melalui penyeragaman fisik termokopel tipe-K. Proses pembuatan 5 unit termokopel tipe-K
berdiameter 0.6 mm dengan variasi ukuran panjang 5200 mm sampai 19000 mm dilakukan
secara manual, yaitu menggunakan metode pilin kawat 4 kali. Pengelasan kedua kaki kawat
termokopel dengan pendekatan celah sebesar 1 mm. Penelitian ini bertujuan untuk
mengetahui karakteristik termokopel tipe-K yang dibuat melalui tahapan pengujian secara
fisik dan perlakuan termal pada suhu 28°C sampai 98°C yang kemudian didinginkan secara
alami. Pengujian gangguan telah diberikan pada saat pemanasan dan pendinginan
berlangsung guna mengetahui respon dari setiap termokopel tipe-K tersebut. Berdasarkan
pengujian tersebut, TC-02 memperoleh nilai kesalahan rerata pengukuran dan deviasi
terbesar dari ke 5 termokopel tipe-K yang dibuat sebesar 1,01% dan 0,0283 secara
berurutan. Hal ini menunjukkan bahwa exposed termokopel tipe-K yang dibuat
menggunakan metode pembuatan dan pengujian seperti ini sudah dapat diintegrasikan ke
dalam sistem untai.
Kata kunci: Termokopel tipe-K, sambungan las, Untai FASSIP-02, kesalahan pengukuran,
deviasi
ABSTRACT
ANALYSIS OF K-TYPE THERMOCOUPLE FABRICATION METHOD IN LOOP OF
FASSIP-02. This passive cooling system assessment is carried out through one of the test
facilities in a hydraulic laboratory called the UNTAI FASSIP-02. There are 32 temperature
measurement points, 1 point measuring flow rate, and operating pressure on the UNTAI
FASSIP-02. After testing at several temperature measurement points, there are several Ktype
thermocouples that experience a decrease in the quality of the reading. In the natural
circulation method, the magnitude of the temperature change of 1°C is significant, so that the
problem of thermocouple reading needs to be followed up. This follow-up was carried out
through physical uniformity of the K-type thermocouple. The fabrication of five K-type
thermocouple units with a diameter of 0.6 mm with a length variation of 5200 mm to 19000
mm is done manually, with using the twisted wire method four times. Welding of both
thermocouple wire legs with a gap approach of 1 mm. This study aims to determine the
characteristics of K-type thermocouples made through physical testing stages and thermal
treatments at temperatures of 28°C to 98°C which are then cooled naturally. Tests for
disturbances have been given during heating and cooling to determine the response of each
K-type thermocouple. Based on these tests, TC-02 obtained the mean value of error
measurement and the largest deviation from the five K-type thermocouples made at 1.01%
and 0.0283 respectively. It shows that the K-type exposed thermocouple which was
fabricated and tested by this method can already be integrated into the loop.
Keywords: Thermocouple type-K, welded joint, FASSIP-02 Loop, measurement error,
deviation