ANALISA FLUKTUASI ARUS KOROSI SAAT HANCURNYA LAPISAN PASIF DAN REPASIFASI OLEH ION KLORIDA

ABSTRAK
ANALISA FLUKTUASI ARUS KOROSI SAAT HANCURNYA LAPISAN PASIF DAN REPASIFASI OLEH
ION KLORIDA. Analisa fluktuasi arus korosi telah menjadi metoda yang penting dalam mempelajari proses
hancur dan repasifasi lapisan pasif pada logam maupun material struktur. Logam atau material yang
mempunyai lapisan pasif pada permukaannya mengalami fluktuasi arus korosi saat proses hancur dan repasifasi
(pembentukan kembali) lapisan pasif. Fluktuasi arus korosi saat hancur dan repasifasi lapisan film dengan dan
tanpa larutan klorida telah diteliti. Telah didapatkan bahwa fluktuasi arus korosi meningkat secara tajam saat
hancurnya lapisan pasif dan menurun saat repasifasi. Fluktuasi arus korosi tidak terdeteksi pada waktu pasifasi
dan saat awal penambahan ion klorida. Dengan analisa fluktuasi arus korosi ini dapat diperkirakan apakah
korosi lubang terjadi pada kondisi tertentu dan kapan terjadinya. Penelitian dilakukan dengan metoda
elektrokimia menggunakan potensiostat.
Katakunci ; repasifasi, lapisan pasif, fluktuasi arus korosi, korosi lubang
ABSTRACT
CORROSION CURRENT FLUCTUATION ANALYSIS DURING PASSIVE FILM BREAKDOWN AND
REPASSIVATION BY CHLORIDE ION. Corrosion current fluctuation becomes an important method in
studying breakdown process and repassivation of passive film on metal and structure material. Metal or material
that has passive film on its surface undergo corrosion current fluctuation during breakdown and repassivation
of passive film. Corrosion current fluctuation during breakdown and repassivation of passive film in with and
without chloride containing solution was studied. It was found that corrosion current fluctuation increased
sharply during breakdown of passive film and reduced sharply during repassivation. Corrosion current
fluctuation was not detected during passivation time and in the beginning of chloride ion addition. Using
corrosion current fluctuation analysis can be predicted weather pitting corrosion occur or not in certain
condition and when it occurs. The experiment has been done through electrocemistry method using potentiostat.
Key words : repassivation, passive film, corrosion current fluctuation, pitting corrosion