PENGUKURAN FLUKS DAN SPEKTRUM NEUTRON 01 FASILITAS DOPING SILIKON RSG-GAS

Amir Hamzah, AH (1996) PENGUKURAN FLUKS DAN SPEKTRUM NEUTRON 01 FASILITAS DOPING SILIKON RSG-GAS. PROSIDING SEMINAR TEKNOLOGI DAN KESELAMATAN PLTN SERTA FASILITAS NUKLIR IV. ISSN 0854-2810

[thumbnail of 0644.pdf]
Preview
Text
0644.pdf

Download (5MB) | Preview

Abstract

Abstrak
PENGUKURAN FLUKS DAN SPEKTRUM NEUTRON 01 FASILITAS
DOPING SILIKON RSG-GAS. Pengukuran fluks dan spektrum neutron di fasilitas
silikon doping RSG-GAS telah dilakukan dengan metode aktivasi keping. Oalam
pengukuran distribusi fluks neutron termal, empat buah keping cobalt-aluminium
dan tiga buah keping nikel diletakkan di tengah kapsul secara berselang-seling
berjarak tiga cm, demikian pula untuk di pinggir kapsul digunakan tiga buah cobaltaluminium
dan ernpat buah kepin';)nikel. Sedangkan pengukuran spektrum neutron
dilakukan di sekitar tengah kapsul yang berdiameter 12,5 cm (5 inci) dart panjang
30 cm menggunakan keping : Co, Cu, Au, Sc, Ag, Fe, Ti, Ni, Mg, AI dan Nb yang
sebagiannya dibungkus cadmium. Hasil pengukuran fluks neutron termal rerata di
pinggir kapsul sebesar 8,26E12 n/cm2s dan ditengah sebesar 7,89E12 n/cm2s,
sedangkan fluks neutron cepat di pinggir kapsul sebesar 3,73E11 n/cm2s dan di
tengah sebesar 3,66E11 n/cm2s. Oengan demikian dapat dikatakan bahwa
distribusi fluks neutron di dalam fasilitas doping silikon RSG-GAS secara radial
cukup merata dengan perbedaan kurang dari 5%. Hasil penentuan fluks neutron
dari hasil pengukuran spektrum neutron pada daerah termal « 0,55 eV yaitu energi
cut-off' cadmium) cukup dekat dengan hasil pengukuran fluks neutron termal di
atas dengan perbedaan sekitar 15%, demikian pula untuk fluks neutron cepat (> 1
MeV yaitu energi efektif keping nikel) dengan perbedaan sekitar 16%.
Abstract
NEUTRON FLUX AND SPECTRUM MEASUREMENT AT SILICON
DOPING FASCILITY OF THE RSG-GAS. Neutron flux and spectrum neasurement
was done using foil activation method. Four cobalt-aluminium and three nickel foils
was lined along capsule centre with 3 cm pitch and three Co-AI and four Ni foils at
the end of capsule. Co, Cu, Au, Sc, Ag, Fe, Ti, Ni, Mg, AI and Nb foils were used for
neutron spectrum measurement around the center of the capsule of 12,5 cm
diamater and 30 cm length.The average of thermal neutron flux in the centre of the
capsule is 7.89E12 n/cm2sand at the end of the capsule is 8.26E12 n/cm2s, and
the average of fast neutron in the centre of the capsule is 3.66E11 n/cm2sand at
the end of capsule is 3.73E11 n/cm2s. Hence, it can be concluded that the radial
distribution of thermal and fast neutron is quite uniform with discrepancy less then
5%. Neutron flux inferred from neutron spectrum mesurement at thermal region «
0,55 eV of cadmium cut-off energy) is quite close to thermal neutron flux
determined from the flux measurement with discrepancy about 15%, and for fast
neutron flux (> 1 MeV of Ni effective energy) the discrepancy is about 16%.

Item Type: Article
Subjects: Taksonomi BATAN > Reaktor Nuklir > Teknologi Reaktor > Fisika Reaktor
Taksonomi BATAN > Reaktor Nuklir > Teknologi Reaktor > Fisika Reaktor
Divisions: BATAN > Pusat Reaktor Serba Guna
IPTEK > BATAN > Pusat Reaktor Serba Guna
Depositing User: Administrator Repository
Date Deposited: 09 Aug 2018 07:59
Last Modified: 02 Jun 2022 02:47