DETEKSI CACAT SAMPEL LAS MATERIAL SA533-B1 BEJANA TEKAN DENGAN METODA UJI TAK RUSAK

Mudi Haryanto, MH and Sri Nitiswati, SN and Andryansyah, AD and Deswandri, DW and Geni Rina Sunaryo, GRS (2017) DETEKSI CACAT SAMPEL LAS MATERIAL SA533-B1 BEJANA TEKAN DENGAN METODA UJI TAK RUSAK. In: Seminar Nasional Teknologi Energi Nuklir 2017, 12 Oktober 2017, Makassar.

[thumbnail of Prosiding-SENTEN-2017.pdf]
Preview
Text
Prosiding-SENTEN-2017.pdf

Download (33MB) | Preview

Abstract

ABSTRAK
DETEKSI CACATSAMPEL LAS MATERIAL SA533-B1 BEJANA TEKAN DENGAN
METODE UJI TAK RUSAK. SA533-B1 adalah materialyang banyak digunakan pada
meterial bejana tekan reaktor PWR. Umumnya pembuatan bejana tekan dilakukan dengan
sambungan las. Untuk mengetahui kualitas pengelasan perlu dilakukan uji mekanik.
Persyaratan sebagai benda uji mekanik adalah pada bagian sampel las dimana akan dibuat
benda uji mekanik harus terbebas dari cacat. Sampel las SA533-B1 di las dengan proses
SMAW. Tujuannya untuk mengetahui ada/tidaknya cacat las pada daerah sambungan yang
di las, sehingga dapat diputuskan kemungkinan dapat/tidaknya sampel uji las dibuat untuk
bahan benda uji mekanik.Metoda yang digunakan adalah uji tak rusak terdiri dari metode
dye penetrant dan metode ultrasonik. Sampel las disediakan sebanyak 3 buah terdiri dari
ukuran (132 x 130 x 12)mm sebanyak 1 buah dan ukuran (300 x 100 x 10)mm sebanyak 2
buah.Hasil dari pengujian dengan metoda dye penetrant dan metoda ultrasonik, pada
sampel las nomor 1 ditemukan cacat porositi dipermukaan dan di dalam las, sampel las
nomor 2 ditemukan cacat retak dipermukaan dan di dalam las, dan sampel nomor 3
ditemukan cacat lack of side wall fusion di dalam las. Semua cacat-cacat tersebut tidak
merata sepanjang sambungan las, sehingga disimpulkan bahwa sampel las dapat dibuat
benda uji mekanik pada daerah yang tidak ada cacatnya.
Kata kunci : Sampel las SMAW, SA533-B1, bejana tekan, uji tak rusak, uji mekanik
ABSTRACT
DETECTION OF SA533-B1 MATERIAL WELD SAMPLE OF PRESSURE VESSEL BY
NON-DESTRUCTIVE METHOD. SA533-B1 is a material widely used in PWR reactor
pressure vessel materials. Generally, the manufacture of pressure vessels made with
welded joints. To determine the quality of the welding necessary mechanical tests. The
requirement as mechanical specimen that is area of weld sample which is mechanical
specimen will be taken should be free from any defects. Weld sample of SA533-B1 has been
welded by SMAW process. The purpose of examination is to know whether any defect or not
on welded area, so can be decide the possibility weld sample to make it as mechanical
specimen. The methods used by non-destructive test such as dye penetrant and ultrasonic
methods. Amount of weld samples are 3 pieces consist of 1 sample with dimension of (132 x
130 x 12) mm, and 2 samples with dimension of (300 x 100 x 10) mm. Results of the test by
the dye penetrant method and the ultrasonic method, in the welded sample number 1 found
porosity defects on the surface and in the weld, the welded sample number 2 found cracked
defects on the surface and in the weld, and sample number 3 found defect lack of side wall
fusion at in welding. All the defects are uneven throughout the weld joint, so it is concluded
that the weld sample can be made mechanical test object in the non-defective area.
Keywords: SMAW weld sample, SA533-B1, pressure vessel, non-destructive testing,
mechanical testing

Item Type: Conference or Workshop Item (Paper)
Subjects: Taksonomi BATAN > Keselamatan dan Keamanan Nuklir
Taksonomi BATAN > Keselamatan dan Keamanan Nuklir
Divisions: BATAN > Pusat Teknologi dan Keselamatan Reaktor Nuklir
IPTEK > BATAN > Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: Administrator Repository
Date Deposited: 08 May 2018 03:53
Last Modified: 31 May 2022 04:35
URI: https://karya.brin.go.id/id/eprint/1154

Actions (login required)

View Item
View Item