PENGEMBANGAN METODE UJI ULTRASONIK UNTUK MEMPREDIKSI SISA UMUR CREEPKOMPONEN (Farokhi,Histori, Roziq Himawan, Andryansyah, Mudi Haryanto)

Farokhi, FK and Histori, His and Roziq Himawan, rh and Andryansyah, AD and Mudi Haryanto, MH (2005) PENGEMBANGAN METODE UJI ULTRASONIK UNTUK MEMPREDIKSI SISA UMUR CREEPKOMPONEN (Farokhi,Histori, Roziq Himawan, Andryansyah, Mudi Haryanto). In: Prosiding Presentasi Ilmiah Teknologi Keselamatan Nuklir X ISSN No. 1410-0533, 26 Pebruari 2003, Pusat Teknologi dan Keselamatan Reaktor Nuklir.

Full text not available from this repository.

Abstract

ABSTRAK
PENGEMBANGAN METODEUJI ULTRASONIK UNTUK MEMPREDIKSI SISA UMUR CREEP KOMPONEN. Telah dikembangkan pendeteksian degradasi creep pada material AISI SUS 304 dengan metode uji ultrsonik. Deteksi ini dimaksudkan untuk mengetahui fenomena yang terjadi selama proses creep berdasarkan perubahan parameter ultrasonik yang berupa atenuasi dan cepat rambat gelombang. Pegujian creep dilakukan pada suhu 600°C dan 40% beban pengujian maksimum dengan memvariasi waktu. Pada pengujian ini yang diukur hanya waktu pemuluran saja sedangkan pertambahan panjang tidak diukur, hal ini dilakukan untuk merepresentasikan kondisi konkrit di lapangan. Dari penelitian ini diketahui bahwaCepat rambat gelombang ultrasonik pada material AISI SUS 304 segar (5928 mm/detik) lebih tinggi dari pada cepat rambat pada material AISI SUS 304 yang mengalami waktu pemuluran 120 jam (5817,121 mm/detik),sedangkan atenuasi pada material segar (0,120144) lebih kecil dari material yang mengalami pemuluran 120 jam (0,138453),
ABSTRACT
DEVELOPMENT OF ULTRASONIC TESTING METHOD TO PREDICT COMPONENT CREEP LIFE TIME. It has been developed the detection of creep degradation of AISI SUS 304 material by ultrasonic testing method. The aim of the detection is to know the creep behaviour of material which may evolve to rupture based on change of ultrasonic parameters such as wave attenuation and velocity. The creep testing was conducted in 600°C with 40% of maximum allowable load on the time variety. The strain of material has not been detected during testing, so the testing based on time rupture only in order to represent reality condition. Based on this research is known that the wave velocity of fresh AISI SUS 304 material (5928 mm/detik) higher than creep treated material for 120 hour (5817,121 mm/detik), whereas the attenuation of fresh material [0.120144] lower then creep treated material [0.13853].

Item Type: Conference or Workshop Item (Paper)
Subjects: Taksonomi BATAN > Keselamatan dan Keamanan Nuklir
Taksonomi BATAN > Keselamatan dan Keamanan Nuklir
Divisions: BATAN > Pusat Teknologi dan Keselamatan Reaktor Nuklir
IPTEK > BATAN > Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: Administrator Repository
Date Deposited: 11 May 2020 05:53
Last Modified: 31 May 2022 03:45
URI: https://karya.brin.go.id/id/eprint/9829

Actions (login required)

View Item
View Item