Two rings of YBa{sub 2}Cu{sub 3}O{sub 7-x} superconductor have been made by using the pressing method, that has been modified. The inner diameter, outer diameter, and thickness of ring 1 are 23.46 mm, 40.66 mm, and 6.84 mm, while for ring 2 are 23.65 mm, 40.73 mm, and 8.28 mm, respectively. The XRD data show that both samples have the same 123-phase. The critical temperature, Tc of both samples is 91 K. The estimate values of induction magnetic field at the center of ring 1 and ring 2 are 1.27 x 10{sup -4} T (I c = 3.48 A) and 1.65 x 10{sup -4} T (I c = 3.52 A), respectively.
Adi, Wisnu Ari;
Sukirman, Engkir;
Winatapura, Didin S;
Handayani, Ari
[1]
- Center for Research and Development of Materials Science and Technology, National Atomic Energy Agency, Serpong (Indonesia)
Citation Formats
Adi, Wisnu Ari, Sukirman, Engkir, Winatapura, Didin S, and Handayani, Ari.
Fabrication And Characterization of YBa{sub 2}Cu{sub 3}O{sub 7-x} Ring For The Laboratory Scale Fault Current Limiter; Pembuatan Dan Karakterisasi Ring YBa{sub 2}Cu{sub 3}O{sub 7-x} Untuk Fault Current Limiter Skala Laboratorium.
Indonesia: N. p.,
2004.
Web.
Adi, Wisnu Ari, Sukirman, Engkir, Winatapura, Didin S, & Handayani, Ari.
Fabrication And Characterization of YBa{sub 2}Cu{sub 3}O{sub 7-x} Ring For The Laboratory Scale Fault Current Limiter; Pembuatan Dan Karakterisasi Ring YBa{sub 2}Cu{sub 3}O{sub 7-x} Untuk Fault Current Limiter Skala Laboratorium.
Indonesia.
Adi, Wisnu Ari, Sukirman, Engkir, Winatapura, Didin S, and Handayani, Ari.
2004.
"Fabrication And Characterization of YBa{sub 2}Cu{sub 3}O{sub 7-x} Ring For The Laboratory Scale Fault Current Limiter; Pembuatan Dan Karakterisasi Ring YBa{sub 2}Cu{sub 3}O{sub 7-x} Untuk Fault Current Limiter Skala Laboratorium."
Indonesia.
@misc{etde_20597677,
title = {Fabrication And Characterization of YBa{sub 2}Cu{sub 3}O{sub 7-x} Ring For The Laboratory Scale Fault Current Limiter; Pembuatan Dan Karakterisasi Ring YBa{sub 2}Cu{sub 3}O{sub 7-x} Untuk Fault Current Limiter Skala Laboratorium}
author = {Adi, Wisnu Ari, Sukirman, Engkir, Winatapura, Didin S, and Handayani, Ari}
abstractNote = {Two rings of YBa{sub 2}Cu{sub 3}O{sub 7-x} superconductor have been made by using the pressing method, that has been modified. The inner diameter, outer diameter, and thickness of ring 1 are 23.46 mm, 40.66 mm, and 6.84 mm, while for ring 2 are 23.65 mm, 40.73 mm, and 8.28 mm, respectively. The XRD data show that both samples have the same 123-phase. The critical temperature, Tc of both samples is 91 K. The estimate values of induction magnetic field at the center of ring 1 and ring 2 are 1.27 x 10{sup -4} T (I c = 3.48 A) and 1.65 x 10{sup -4} T (I c = 3.52 A), respectively.}
journal = {Indonesian Journal of Materials Science}
issue = {2}
volume = {5}
journal type = {AC}
place = {Indonesia}
year = {2004}
month = {Feb}
}
title = {Fabrication And Characterization of YBa{sub 2}Cu{sub 3}O{sub 7-x} Ring For The Laboratory Scale Fault Current Limiter; Pembuatan Dan Karakterisasi Ring YBa{sub 2}Cu{sub 3}O{sub 7-x} Untuk Fault Current Limiter Skala Laboratorium}
author = {Adi, Wisnu Ari, Sukirman, Engkir, Winatapura, Didin S, and Handayani, Ari}
abstractNote = {Two rings of YBa{sub 2}Cu{sub 3}O{sub 7-x} superconductor have been made by using the pressing method, that has been modified. The inner diameter, outer diameter, and thickness of ring 1 are 23.46 mm, 40.66 mm, and 6.84 mm, while for ring 2 are 23.65 mm, 40.73 mm, and 8.28 mm, respectively. The XRD data show that both samples have the same 123-phase. The critical temperature, Tc of both samples is 91 K. The estimate values of induction magnetic field at the center of ring 1 and ring 2 are 1.27 x 10{sup -4} T (I c = 3.48 A) and 1.65 x 10{sup -4} T (I c = 3.52 A), respectively.}
journal = {Indonesian Journal of Materials Science}
issue = {2}
volume = {5}
journal type = {AC}
place = {Indonesia}
year = {2004}
month = {Feb}
}