KETAHANAN KOROSI PADUAN Al-Mg 5052 DI DALAM AIR PENDINGIN NETRAL MENGANDUNG KLORIDA

Dicky Trijatmiko, DT and Isdiriayani Nurdin, IN and Hery Devianto, HD (2015) KETAHANAN KOROSI PADUAN Al-Mg 5052 DI DALAM AIR PENDINGIN NETRAL MENGANDUNG KLORIDA. Urania, 22 (2). ISSN 0852-4777

[thumbnail of 2263] Text
2263

Download (97kB)

Abstract

KETAHANAN KOROSI PADUAN Al-Mg 5052 DI DALAM AIR PENDINGIN NETRAL MENGANDUNG KLORIDA. Paduan Al-Mg 5052 adalah material yang biasa digunakan untuk kelongsong elemen bakar nuklir karena serapan fluks netronnya rendah dan tahan korosi di dalam air demineralisasi pada kondisi operasi reaktor. Makalah ini difokuskan untuk mengetahui ketahanan korosi paduan Al-Mg 5052 di dalam air dengan pH netral dan mengandung klorida sebagai pengganti air demineralisasi pendingin primer Reaktor Serba Guna GA Siwabessy (RSG-GAS). Penelitian mencakup pengukuran laju korosi menggunakan metode Tafel, prediksi mekanisme korosi menggunakan metode voltametri siklik dan analisa produk korosi dengan metode difraksi sinar X. Percobaan dilakukan dengan variasi temperatur 30°C, 35°C, 40°C, dan 45°C, serta variasi konsentrasi larutan natrium klorida 0,05 M, 0,25 M, dan 0,5 M. Hasil penelitian ini menunjukkan bahwa paduan Al-Mg 5052 terkorosi dengan kategori “dapat diabaikan” hingga “sedang” dalam larutan natrium klorida menjadi produk yang larut dalam air pada satu tahap reaksi oksidasi irreversible.

CORROSION RESISTANCE OF Al-Mg ALLOY 5052 IN CHLORIDE CONTAINING NEUTRAL COOLING WATER. Al-Mg alloy 5052 is a material used as nuclear fuel element cladding due to its low neutron flux absorption and high corrosion resistance in demineralized water. This research is focused to know of the corrosion resistance of Al-Mg alloy 5052 in chloride containing neutral water used as demineralized primary cooling water substitute in GA Siwabessy Multi Purpose Reactor (RSG-GAS). This research covers the corrosion rate measurement using the Tafel method, corrosion process prediction using cyclic voltammetry method and corrosion product analysis using X-Ray Diffraction method. The experiments are carried out at temperature variation of 30°C, 35°C, 40°C and 45°C, as well as sodium chloride concentration of 0.05 M, 0.25 M and 0.5 M. The research results show that Al-Mg alloy 5052 is insignificantly to moderate corroded in chloride containing water by single step irreversible oxidation reaction.

Item Type: Article
Subjects: Taksonomi BATAN > Reaktor Nuklir > Pemanfaatan Reaktor > Eksperimen Reaktor
Taksonomi BATAN > Reaktor Nuklir > Pemanfaatan Reaktor > Eksperimen Reaktor
Divisions: BATAN > Pusat Reaktor Serba Guna
IPTEK > BATAN > Pusat Reaktor Serba Guna
Depositing User: Administrator Repository
Date Deposited: 29 Oct 2018 02:01
Last Modified: 31 May 2022 04:51
URI: https://karya.brin.go.id/id/eprint/4073

Actions (login required)

View Item
View Item