Sarwani, Sarwani and Suroso, S and Suwoto, Suwoto and Pranto Busono, PB (1999) KARAKTERISASI KAPSUL RABBIT JENIS POLYETHYLENE NAPHTHALENE. PROSIDING SEMINAR HASIL PENELITIAN PRSG. ISSN 0854-5278
Sarwani.pdf
Download (3MB) | Preview
Abstract
KARAKTERISASI KAPSUL RABBIT JENIS POL YETHYLENE NAPHTHALENE. Polyethylene Naphthalene (PEN) merupakan polimer jenis plastik yang mempunyai titik leleh 273°C (lebih tinggi dari Polyethylene). PEN akan dipergunakan sebagai bahan kapsul yang akan diiradiasi di fasilitas iradiasi sistem rabbit denganjlllence neutron besar. Pengujian kapsul PEN telah dlakukan dengan mengiradiasi kapsul PEN pada jlllence neutron bervariasi, mengukur laju dosis radiasinya, menganalisis unsur pengotor yang terkandung dalam kapsul clan selanjutnya dilakukan uji kerapuhan. Hasil pengujian menunjukkan bahwa kapsul PEN tahan diiradiasi sampai jlllence neutron 2,8xI017 n/cm2 dengan laju dosis kapsul PEN setelah peluruhan 1 jam padajarak 0 m adalah 1460 /-lGyclanpadajarak 1 meteradalah 153 ~LGy.Unsur pengotor yang terkandung dalam kapsul PEN adalah Na, AI, Zn, Sb, Mn, Cr, Cu, Sn clan Ti. Hasil uji kerapuhan kapsul PEN yang teriradiasi padajlllence neutron 2,8xI017 n/cm2 adalah 2 kJ/m2. Dari basil pengujian tersebut di atas menunjukkan bahwa kapsul PEN tahan untuk diiradiasi sampai jlllence neutron 2,8x1017 n/cm2 (6 jam) pada daya 15 MW. Untuk keselamatan pekerja makapenanganan kapsul PEN hams dilakukan di dalam Hot Cell.
ABSTRACT CHARACTERITATION OF THE POLYETHYLENE NAPHTHALENE CAPSULE.Polyethylene Naphthalene ( PEN) is a plastic polymer with melting point of 273°c. The PEN will be used for capsule material and irradiated in the rabbit system facility dealing with high neutronjlllence. The characteritation test of the PEN capsule has been carried out at varied neutron jlllence and then followed by radiation measurement, analysis of the impurities in the capsule material and brittle test of the capsule. The result shows that PEN capsule can be applied atneutronjlllence of 2.8 x 1017 n/cm2. The radiation dose after I-hour of cooling down is 1460/-lGy at O-meter and 153 /-lGyat I-meter. The impurities in the capsule material are Na, AI, Zn, Sb, Mn, Cr, Cu, Sn and Ti. The capsule brittle test is ~ 17 ~ . 2 kJ/m~ at neutronjlllence of 2.8 x 10 n/cm~. The handlmg of the PEN capsule must be carried out in the hot cell
Item Type: | Article |
---|---|
Subjects: | Taksonomi BATAN > Reaktor Nuklir > Pemanfaatan Reaktor > Eksperimen Reaktor Taksonomi BATAN > Reaktor Nuklir > Pemanfaatan Reaktor > Eksperimen Reaktor |
Divisions: | BATAN > Pusat Reaktor Serba Guna IPTEK > BATAN > Pusat Reaktor Serba Guna |
Depositing User: | Administrator Repository |
Date Deposited: | 20 Sep 2018 07:49 |
Last Modified: | 02 Jun 2022 02:43 |
URI: | https://karya.brin.go.id/id/eprint/3993 |