AIP Conference Proceedings 989, 85 (2008); https://doi.org/10.1063/1.2906101
more...View Affiliations
  • Neutron Scattering Laboratory, Center of Technology for Nuclear Industrial Materials National Nuclear Energy Agency of Indonesia—BATAN, Kawasan Puspiptek Serpong, Tangerang 15314, Indonesia
Analysis of bulk aluminum A‐1050 has been performed using FCD/TD‐BATAN. From neutron diffraction pattern of bulk sample, two Bragg peaks, (220) and (200) are observed while three Bragg peaks of (111), (311) and (222) are over dumped. Due to preferred orientation, crystallites are highly oriented to 〈110〉 direction. Texture analysis for pole figure reconstruction is performed for (200) and (220). From analysis result using MAUD program, a goodness of fitting (σ = 1.259), crystallographic weighted error (Rw = 32.81%) and texture error (Rp = 19.03%) are obtained. Analysis of powder type of A‐1050 is also carried out. From neutron diffraction measurement, Bragg peaks of (111), (200), (220), (311) and (222) are observed with highest intensity at (111). From analysis result σ = 1.008, and Rw = 16.68% are obtained.

Select Your Access


Purchase

Standard PPV for $30.00